This epoxy system is designed for medium and high Tg pultrution processes.
This epoxy system is designed for medium and high Tg pultrution processes.
SWANCOR 2209-A/B is two-component epoxy system. It has excellent pot life with low viscosity and also quick cure rate at elevated temperatures. Higher Tg (glass transition temperature)and better heat resistance. Easy demolding process brings perfect surface quality.
These features coupled with excellent adhesion to several reinforcement including glass and carbon fiber make it excellent choice for pultrusion applications.
|
1.SWANCOR 2209-A packed 5 gallon barrel, weight 20kg per barrel.
2.SWANCOR 2209-B packed 5 gallon barrel, weight 18kg per barrel.
3.The epoxy and hardener have to well mix by regular proportion for use.
4.After epoxy and hardener are mixed, it should be used in valid period, in case it gels and can’t be use.
5.All implement for daubing and stowing should be cleansed right after used.
6.Under construction duration, should avoid skin contact, wear protective cloth and glove if necessary.
Items | Unit | 2209–A/B | Standard |
Tensile Strength | MPa | 65~75 | ASTM D 638 or ISO 527 |
Tensile Modulus | GPa | 2.5~3.0 | ASTM D 638 or ISO 527 |
Elongation of Break | % | 3~5 | ASTM D 638 or ISO 527 |
Flexural Strength | MPa | 120~130 | ASTM D 790 or ISO 178 |
Flexural Modulus | GPa | 2.5~3.0 | ASTM D 790 or ISO 178 |
Tg |
℃ |
150~160 |
DSC 10℃/min |
Curing Condition:90℃1hr+120℃1hr+160℃4hr