Expoxy Resin Pultrution Swancor 2210 A/B

This epoxy system is designed for high Tg requirements pultrution processes.


Product Description

SWANCOR 2210-A/B is a two component epoxy based resin system for pultrusion and filament winding application. This system  combined  low  viscosity  ,  high  reactivity  and  good wet-out properties with glass fibers and carbon fibers. With proper controlled high temperature fabrication process (150~200°C), high Tg above 200°C (DSC Method) can be achieved.


Typical properties of liquid resin


Property Unit SWANCOR




Appearance Light yellowish


Light Brown


Viscosity @ 25℃ Cps 250~350 150~250
Mixed ratio(by wt). A:B=100:150
Mixed viscosity Cps 220~320
Density(g/cm3) % 1.10~1.20 1.15~1.25
Shelf life year 1 1

Curing properties*1


Property Unit Liquid Resin
Gel time @ 150°C minutes 2.5~3.5
Gel time @ 180°C seconds 40~60

*10.5g mixed resin on hot plate


Mechanical Properties of Resin Casting


Ingredients Unit Value Rate
Tensile strength MPa 50-60 ASTM D 638
Tensile modulus GPa 2.1 – 2.3 ASTM D 638
Elongation at

tensile strength




2.5 – 3.5


ASTM D 638

Flexural strength MPa 100 – 110 ASTM D 790
Flexural modulus GPa 2.1 – 2.3 ASTM D 790
Glass transition







(DSC 20℃/min)



SWANCOR 2210-A were packed in 5gallon barrel, weight 20kg per barrel. SWANCOR 2210-B were packed in 5 gallon barrel, weight 15kg per barrel.

contaminated clothing before re-use.


Flush with large amount of water immediately and continuously for 20 minutes, lifting upper and lower lids occasionally. Get medical attention.


Do not induce vomiting. Keep person warm, quiet  and get medical  attention.  Aspiration of material  into the  lungs  can cause chemical pneumonitis which can be fatal.


If affected, remove individual to fresh air. If breathing is difficult, administer oxygen. If breathing has stopped, give artificial respiration. Keep person warm, quiet, and get medical attention. PERSONAL PROTECTION

Do not breathe vapors. Vapor explosion hazard, keep out of sewers. Eliminate all sources of ignition in Vicinity of spill or released Vapor to avoid fire or explosion. For large spills, warn public   of   downwind  explosion   hazard.   Check   area   with explosion meter before reentering area. Ground and bond all containers and handling equipment.


Keep away from ignition sources; flames, pilot lights, electrical sparks, and sparking tools. NO SMOKING. Do not store in direct sunlight. To ensure maximum stability and maintain optimum resin properties, resins should be stored in closed containers at temperatures below 25℃ (77oF).


Eliminate  all  ignition sources  (flares,  flames,  including  pilot lights electrical sparks). Persons not wearing protective equipment should be exclude from area of spill until clean-up has been completed. Stop spill at source, dike area of spill to prevent  spreading, pump liquid to salvage tank. Remaining liquid may be taken up on sand, clay, earth, floor absorbent or other absorbent material and shoveled into containers.


Destroy by liquid incineration in accordance with applicable regulation. Contaminated absorbent should be disposed in accordance to government regulations.


Thoroughly   wash   exposed   area   with   soap   and   water immediately.    Remove    contaminated    clothing.


    Ficha Técnica y de Seguridad

    Mantendremos tus datos solo mientras lo desees. Siempre estarán seguros y puedes editarlos o dejar de recibir nuestros mensajes cuando quieras.

      Más Información

      Responsable: Global Composites, S.L. Finalidad: Poder contestarle al mensaje que nos envíe al enviar dicho formulario Legitimación: Su conocimiento Destinatarios: Sus datos se guardaran en nuestro proveedor de hosting, y que también cumple con la RGDP Derechos: Tendrá derecho, entre otros, a acceder, rectificar, limitar y suprimir sus datos cuando lo desee.